TL-1539B
TAILAI
3506990000
1) Advantage:
A)It has excellent adhesion to foam substrates such as PE, PU, and rubber-plastic composites
B)Excellent high temperature property
C)Adhesive-resistant curved surfaces, ensuring secure attachment to HDPE and sheet metal curved surfaces
D)Low VOC, low odor
2) Physical property:
Item | Property/data |
appearance | Light yellow transparent viscous liquid |
composition | Polymer, ethyl acetate |
solid | 50±2% |
Viscosity （adjustable) | 1000～5000cps |
3) Usage Instructions
A.) single component, with moderate viscosity, suitable for direct coating;
B.) Coating conditions: Hot air drying at 80°C for 2-4 minutes (Note: Ensure complete solvent evaporation);
C) To avoid affecting performance, testing should be conducted after stabilizing at 23°C for 3 days after-coating.
4)Application property
Test item | Product structure |
Standard | |
Release materialAD=25 μm25 μm PET
| Release materialAD=55 μm5mmPU Sponge
| ||
Peel strength （g/25mm） | 1400 | / | GB/T 2792-1998 |
Initial tack（#） | 8 | 32 | GB/T 4852-2002 |
Holding power （mm） | 0.3 | 23℃×500g ≥30min not fall off | GB/T4851-1998 60℃×1kg×1h |
Durable surface Self curling | / | Brushing does not bounce open | 23℃×72h/ 0℃×72h |
Durable surface exhaust duct | / | Brushing does not bounce open | 23℃×72h/ 0℃×72h |
Face to face sticking test | / | Substrate broken | Adhesive surface sticking, tear off quickly |
Comment：
All data in this document were tested under laboratory standard conditions, and the data are typical test values, not guaranteed values.
Special Note
When selecting products, please fully evaluate the production conditions and application scenarios. If you encounter any problems, please contact our technical service department, and we will be dedicated to providing you with services. |